Hot Dip Galvanizing

Specifications

GALVANIZING

The main steps of the galvanizing process are

1- Cleaning Cycle (degreasing, rinsing, picking, rinsing)

We have been fabricating quality high mast with raising and lowering gear system , These poles is a safe system due to reliable service hoist which raises and lowers the fixtures ring for maintenance purposes.

2- Fluxing

Fluxing is the final surface preparation step in the galvanizing process. Fluxing removes oxides and prevents further oxides from forming on the surface of the metal prior to galvanizing.

3- Galvanizing

In this step, the material is completely immersed in a bath consisting of a minimum of 98% pure molten zinc. The bath temperature is maintained at about 840 F (449 C). Fabricated items are immersed in the bath until they reach bath temperature. The zinc metal then reacts with the iron on the steel surface to form a zinc/iron intermetallic alloy.
INSPECTION – A variety of simple physical and laboratory tests may be performed to determine thickness, uniformity, adherence and appearance. Products are galvanized according to long established, well-accepted, and approved standards of ASTM A123/A123M, AS/NZS 4680, and BS EN ISO 1461.

4- Post-Treatment (quenching & passivity)

The post-galvanization treatment includes quenching the material with water or air cooling. Conditions in the galvanizing plant such as temperature, humidity, and air quality do not affect the quality of the galvanized material’s appearance. The component is finally dipped in the passivity tank to prevent wet storage stains or white rust,
You are now left with a beautifully spangled product, setting it apart in quality and appearance. Here at Galva Coat, we are proud to protect your product, and in turn, protect you and your company from unseen future maintenance costs.